Utilization of Parawood Ash in Concrete Paving Blocks
Article Sidebar
Published:
Apr 27, 2020
Keywords:
concrete paving block parawood ash compressive strength water absorption curing
Main Article Content
Abstract
This research was conducted to study the use of parawood ash (PWA) as the replacement of Portland cement type 1 in producing concrete paving blocks. The mixtures of PWA which contain 0, 10, 20 and 30% by weight of binder were examined in this study. The control variable is the ratio between water and binder material (0.330, 0.365, 0.405 and 0.455). The compressive strength of the concrete blocks was tested on different curing periods of 7, 14, 28 days and the water absorption at 28 days. The result showed that the increasing amount of PWA decreased the compressive strength but increased water absorption. The concrete blocks using PWA toreplace Portland cement type 1 at 10 and 20 percent meet the standard of TIS. 827-2531 and TIS. 2035-2543,respectively.
Article Details
How to Cite
Klathae , T., Sornpakdee, N., Buathongkhue, C., & Deedard, N. (2020). Utilization of Parawood Ash in Concrete Paving Blocks. Rajamangala University of Technology Srivijaya Research Journal, 12(1), 36–48. Retrieved from https://li01.tci-thaijo.org/index.php/rmutsvrj/article/view/241931
Section
Research Article
The content and information in the article published in Journal of Rajamangala University of Technology Srivijaya It is the opinion and responsibility of the author of the article. The editorial journals do not need to agree. Or share any responsibility.
References
กันยาพร เหลืองวิสุทธิ์ศิริ. 2546. การศึกษาการใช้ขี้เถ้าแกลบผสมปูนซีเมนต์ในการทำบล็อกปูพื้น. วิทยานิพนธ์ปริญญาวิศวกรรมศาสตรมหาบัณฑิต สาขาเทคโนโลยีสิ่งแวดล้อม คณะพลังงานและวัสดุ, มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี.
เผ่าพงศ์ นิจจันทร์พันธ์ศรี และ ประชุม คำพุฒ. 2548. รายงานการวิจัย การใช้หินฝุ่นผสมคอนกรีตแทนทราย. มหาวิทยาลัยเทคโนโลยีราชมงคลธัญบุรี.
ปริญญา จินดาประเสริฐ และ ชัย จาตุรพิทักษ์กุล. 2555. ปูนซีเมนต์ ปอซโซลาน และคอนกรีต. พิมพ์ครั้งที่ 7. สมาคมคอนกรีตแห่งประเทศไทย, กรุงเทพฯ.
วินิต ช่อวิเชียร. 2539. คอนกรีตเทคโนโลยี. พิมพ์ครั้งที่ 8. ห้างหุ้นส่วนจำกัด ป.สัมพันธ์พาณิชย์, กรุงเทพฯ.
ศูนย์วิจัยกสิกรไทย. 2558. ฝ่าวิกฤติยางพาราไทยปี 2558: ทางเลือก&ทางรอดของชาวสวนยางท่ามกลางแรงกดดันด้านราคา. ศูนย์วิจัยกสิกรไทย. แหล่งที่มา: http://library.dip.go.th/multim6 /edoc/2558 /24084 .pdf, 30 มิถุนายน 2560.
สำนักงานมาตรฐานผลิตภัณฑ์อุตสาหกรรม. 2531. มาตรฐานผลิตภัณฑ์อุตสาหกรรมคอนกรีตบล็อกประสานปูพื้น. มอก. 827-2531, สำนักงานมาตรฐานผลิตภัณฑ์อุตสาหกรรม. แหล่งที่มา: https://WWW.tisi.go.th/data /PR/pdf/ R827 _2531_00.pdf, 26 มิถุนายน 2560.
สำนักงานมาตรฐานผลิตภัณฑ์อุตสาหกรรม. 2543. มาตรฐานผลิตภัณฑ์อุตสาหกรรมคอนกรีตบล็อกประสานปูพื้นสำหรับงานหนัก. มอก.2035-2543, สำนักงานมาตรฐานผลิตภัณฑ์อุตสาหกรรม. แหล่งที่มา: https:// WWW.tisi.go.th/data /PR/pdf/R2035_2543_00.pdf, 14 มิถุนายน 2560.
สำนักงานปลัดกระทรวงมหาดไทย. 2560. ข้อมูลนโยบายด้านการเกษตร ปี 2560. แหล่งที่มา: http://WWW.mukdahan.go.th/muk_download/pdf/428.pdf, 30 มิถุนายน 2561.
สำนักวิจัยเศรษฐกิจการเกษตร. 2556. สถานการณ์สินค้าเกษตรที่สำคัญและแนวโน้ม ปี 2557. แหล่งที่มา: http://WWW.oae.go.th/assets/portals/1/files/ebook/OAEAnnual2556.pdf, 30 มิถุนายน 2560.
สุวัฒนา นิคม. 2553. คุณลักษณะของยิปซั่มเพสต์โดยใช้ยิปซั่มเทียมเถ้าลอยไม้ยางพาราและดินขาวแปร. วิทยานิพนธ์วิศวกรรมศาสตรมหาบัณฑิต, มหาวิทยาลัยสงขลานครินทร์.
อาบีเด็ง ฮาวา และ ดนุพล ตันนโยภาส. 2551. ผลกระทบของเถ้าลอยไม้ยางพาราที่มีต่อสมบัติของคอนกรีตมวลรวมพัมมิซ, น. 43-48. ใน การประชุมวิชาการทางวิศวกรรมศาสตร์ ครั้งที่ 6. มหาวิทยาลัยสงขลานครินทร์, สงขลา.
อาบีเด็ง ฮาวา. 2551. สมบัติของคอนกรีตมวลเบาหินพัมมิซผสมเถ้าลอยไม้ยางพาราและเถ้าแกลบ. วิทยานิพนธ์วิศวกรรมศาสตรมหาบัณฑิต, มหาวิทยาลัยสงขลานครินทร์.
อาบีดีน ดะแซสาเมาะ, จินดา มะมิง, โนรีสะ ราแดง และ ยาเซ็ง อาแว. 2554. สมบัติทางกายภาพและสมบัติทางกลของอิฐที่มีส่วนผสมของเถ้าไม้ยางพารา. วารสารมหาวิทยาลัยราชภัฎยะลา 6(1): 25-35.
อาบีดีน ดะแซสาเมาะ, ฮาปือเสาะ มาหะ และ ฮาลีเมาะ เจ๊ะบือราเฮง. 2557. สมบัติของอิฐบล็อกประสานจากเถ้าไม้ยางพาราผสมดินขาวนราธิวาส. วารสารหน่วยวิจัยวิทยาศาสตร์ เทคโนโลยี และสิ่งแวดล้อมเพื่อการเรียนรู้ 5(2): 202-208.
ASTM. 2001. ASTM C136-96a. Standard Test Method for Sieve Analysis of Fine and Coarse Aggregates. Annual Book of ASTM Standards. American Society for Testing and Materials, West Conshohocken, PA.
ASTM. 2007. ASTM C29. Standard Test Method for Unit Weight of Aggregate. Annual Book of ASTM Standards. American Society for Testing and Materials, West Conshohocken, PA.
ASTM. 2008. ASTM C618-08a. Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete. Annual Book of ASTM Standards. American Society for Testing and Materials, West Conshohocken, PA.
ASTM. 2009. ASTM C188. Standard Test Method for Density of Hydraulic Cement. Annual Book of ASTM Standards. American Society for Testing and Materials, West Conshohocken, PA.
ASTM. 2011. ASTM C33/C33M-11. Standard Specification for Concrete Aggregates. Annual Book of ASTM Standard. American Society for Testing and Materials, West Conshohocken, PA.
ASTM. 2014. ASTM C230/C230M-14. Standard Specification for Flow Table for Use in Test of Hydraulic Cement. Annual Book of ASTM Standards. American Society for Testing and Materials, West Conshohocken, PA.
ASTM. 2015. ASTM C128-15. Standard test method for relative Density (Specific Gravity) and Absorption of Fine Aggregate. Annual Book of ASTM Standards. American Society for Testing and Materials, West Conshohocken, PA.
เผ่าพงศ์ นิจจันทร์พันธ์ศรี และ ประชุม คำพุฒ. 2548. รายงานการวิจัย การใช้หินฝุ่นผสมคอนกรีตแทนทราย. มหาวิทยาลัยเทคโนโลยีราชมงคลธัญบุรี.
ปริญญา จินดาประเสริฐ และ ชัย จาตุรพิทักษ์กุล. 2555. ปูนซีเมนต์ ปอซโซลาน และคอนกรีต. พิมพ์ครั้งที่ 7. สมาคมคอนกรีตแห่งประเทศไทย, กรุงเทพฯ.
วินิต ช่อวิเชียร. 2539. คอนกรีตเทคโนโลยี. พิมพ์ครั้งที่ 8. ห้างหุ้นส่วนจำกัด ป.สัมพันธ์พาณิชย์, กรุงเทพฯ.
ศูนย์วิจัยกสิกรไทย. 2558. ฝ่าวิกฤติยางพาราไทยปี 2558: ทางเลือก&ทางรอดของชาวสวนยางท่ามกลางแรงกดดันด้านราคา. ศูนย์วิจัยกสิกรไทย. แหล่งที่มา: http://library.dip.go.th/multim6 /edoc/2558 /24084 .pdf, 30 มิถุนายน 2560.
สำนักงานมาตรฐานผลิตภัณฑ์อุตสาหกรรม. 2531. มาตรฐานผลิตภัณฑ์อุตสาหกรรมคอนกรีตบล็อกประสานปูพื้น. มอก. 827-2531, สำนักงานมาตรฐานผลิตภัณฑ์อุตสาหกรรม. แหล่งที่มา: https://WWW.tisi.go.th/data /PR/pdf/ R827 _2531_00.pdf, 26 มิถุนายน 2560.
สำนักงานมาตรฐานผลิตภัณฑ์อุตสาหกรรม. 2543. มาตรฐานผลิตภัณฑ์อุตสาหกรรมคอนกรีตบล็อกประสานปูพื้นสำหรับงานหนัก. มอก.2035-2543, สำนักงานมาตรฐานผลิตภัณฑ์อุตสาหกรรม. แหล่งที่มา: https:// WWW.tisi.go.th/data /PR/pdf/R2035_2543_00.pdf, 14 มิถุนายน 2560.
สำนักงานปลัดกระทรวงมหาดไทย. 2560. ข้อมูลนโยบายด้านการเกษตร ปี 2560. แหล่งที่มา: http://WWW.mukdahan.go.th/muk_download/pdf/428.pdf, 30 มิถุนายน 2561.
สำนักวิจัยเศรษฐกิจการเกษตร. 2556. สถานการณ์สินค้าเกษตรที่สำคัญและแนวโน้ม ปี 2557. แหล่งที่มา: http://WWW.oae.go.th/assets/portals/1/files/ebook/OAEAnnual2556.pdf, 30 มิถุนายน 2560.
สุวัฒนา นิคม. 2553. คุณลักษณะของยิปซั่มเพสต์โดยใช้ยิปซั่มเทียมเถ้าลอยไม้ยางพาราและดินขาวแปร. วิทยานิพนธ์วิศวกรรมศาสตรมหาบัณฑิต, มหาวิทยาลัยสงขลานครินทร์.
อาบีเด็ง ฮาวา และ ดนุพล ตันนโยภาส. 2551. ผลกระทบของเถ้าลอยไม้ยางพาราที่มีต่อสมบัติของคอนกรีตมวลรวมพัมมิซ, น. 43-48. ใน การประชุมวิชาการทางวิศวกรรมศาสตร์ ครั้งที่ 6. มหาวิทยาลัยสงขลานครินทร์, สงขลา.
อาบีเด็ง ฮาวา. 2551. สมบัติของคอนกรีตมวลเบาหินพัมมิซผสมเถ้าลอยไม้ยางพาราและเถ้าแกลบ. วิทยานิพนธ์วิศวกรรมศาสตรมหาบัณฑิต, มหาวิทยาลัยสงขลานครินทร์.
อาบีดีน ดะแซสาเมาะ, จินดา มะมิง, โนรีสะ ราแดง และ ยาเซ็ง อาแว. 2554. สมบัติทางกายภาพและสมบัติทางกลของอิฐที่มีส่วนผสมของเถ้าไม้ยางพารา. วารสารมหาวิทยาลัยราชภัฎยะลา 6(1): 25-35.
อาบีดีน ดะแซสาเมาะ, ฮาปือเสาะ มาหะ และ ฮาลีเมาะ เจ๊ะบือราเฮง. 2557. สมบัติของอิฐบล็อกประสานจากเถ้าไม้ยางพาราผสมดินขาวนราธิวาส. วารสารหน่วยวิจัยวิทยาศาสตร์ เทคโนโลยี และสิ่งแวดล้อมเพื่อการเรียนรู้ 5(2): 202-208.
ASTM. 2001. ASTM C136-96a. Standard Test Method for Sieve Analysis of Fine and Coarse Aggregates. Annual Book of ASTM Standards. American Society for Testing and Materials, West Conshohocken, PA.
ASTM. 2007. ASTM C29. Standard Test Method for Unit Weight of Aggregate. Annual Book of ASTM Standards. American Society for Testing and Materials, West Conshohocken, PA.
ASTM. 2008. ASTM C618-08a. Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete. Annual Book of ASTM Standards. American Society for Testing and Materials, West Conshohocken, PA.
ASTM. 2009. ASTM C188. Standard Test Method for Density of Hydraulic Cement. Annual Book of ASTM Standards. American Society for Testing and Materials, West Conshohocken, PA.
ASTM. 2011. ASTM C33/C33M-11. Standard Specification for Concrete Aggregates. Annual Book of ASTM Standard. American Society for Testing and Materials, West Conshohocken, PA.
ASTM. 2014. ASTM C230/C230M-14. Standard Specification for Flow Table for Use in Test of Hydraulic Cement. Annual Book of ASTM Standards. American Society for Testing and Materials, West Conshohocken, PA.
ASTM. 2015. ASTM C128-15. Standard test method for relative Density (Specific Gravity) and Absorption of Fine Aggregate. Annual Book of ASTM Standards. American Society for Testing and Materials, West Conshohocken, PA.