Development of clay brick process with glass cullet addition
Article Sidebar
Main Article Content
Abstract
This research aimed to study the effect of glass cullet addition on the physical and mechanical properties of fired clay brick. Glass cullet was added in the mixture at 5, 10, 15 and 20 wt%. It was then fired at 900, 1,000 and 1,100 °C for 1 hour. The result found that shrinkage value of samples increased significantly with the increasing temperature, which related with higher densification. Moreover, the porosity of samples was improved that affected on high compressive strength value. In the glass cullet additive part, higher glass cullet addition led to melted glassy phase in clay particles, so the densification was improved. Therefore, the compressive strength value tended to increase with higher glass cullet addition. Based on the result of this research, it confirmed that glass culler addition could be applied in fired clay brick
Article Details
The content and information in the articles published in the Journal of Science and Technology, Sisaket Rajabhat University reflect the opinions and responsibilities of the respective authors. The editorial board of the journal does not necessarily agree with, nor share responsibility for, these views.
Articles, information, content, images, etc., published in the Journal of Science and Technology, Sisaket Rajabhat University are copyrighted by the Faculty of Science and Technology, Sisaket Rajabhat University. If any individual or organization wishes to republish all or part of the content, or use it for any other purpose, they must obtain written permission from the Journal of Science and Technology, Sisaket Rajabhat University beforehand.
References
พานทอง อินทรชัย. คุณสมบัติเชิงกลและเชิงความร้อนของอิฐดินเหนียวผสมเถ้าลอยและยิปซัมจากโรงไฟฟ้าแม่เมาะ. [วิทยานิพนธ์วิศวกรรมศาสตร์มหาบัณฑิต]. มหาวิทยาลัยเชียงใหม่; 2548.
Broown, I.W., and Mackenzie, K.J.D., Process desing for the production of a ceramic-like body from recycled waste glass. Part 1. The effect of fabrication variables on green strength. Journal of Materials Science, 1982; 17: 2164-2170.
Luz, A.P., and Ribeiro, S. Use of glass waste as a raw material in porcelain stoneware tile mixtures. Ceramics International, 2007; 33: 761-765.
Dondi, M., Guarini, G., Raimondo, M., Zanelli, C. Recycling PC and TV waste glass in clay bricks and roof tiles. Waste Management, 2009; 29: 1945-1951.
เอก ช่อประดับ. คุณสมบัติเชิงกายภาพของอิฐสามัญที่ทำจากดินเหนียวผสมแกลบ. [วิทยานิพนธ์ปริญญาโท].มหาวิทยาลัยเชียงใหม่; 2547.
Loryuenyong, V., Panyachai, T., Kaewsimork, K., Siritai, C., Effects of recycled glass substitution on the physical and mechanical properties of clay brick. Waste Management 2009; 29: 2727-2721.
Chidiac, S.E., and Federico L.M. Effects of waste glass addition on the properties and durability of fired clay brick. Canadian Journal of Civil Engineering, 2007; 34: 1458-1466.
ไพจิตร อิ่งศิริวัฒน์. เนื้อดินเซรามิก. สำนักพิมพ์โอเดียนสโตร์ กรุงเทพมหานคร. 2541.
Demir, I. Reuse of waste glass in building brick production. Waste Management and Research, 2009; 27: 572-577.
พานทอง อินทรชัย. คุณสมบัติเชิงกลและเชิงความร้อนของอิฐดินเหนียวผสมเถ้าลอยและยิปซัมจากโรงไฟฟ้าแม่เมาะ. [วิทยานิพนธ์วิศวกรรมศาสตร์มหาบัณฑิต]. มหาวิทยาลัยเชียงใหม่; 2548.